Wood Basics

Sitka spruce is the most common wood used in aircraft, and contrary to popular belief, Howard Hughes’ Spruce Goose was made of birch-not spruce. Spruce has one of the greatest strength-to-weight ratios and is considered the cream of the crop of natural aircraft building materials. Western hemlock is 14 percent stronger and can be substituted for spruce, according to FAA Advisory Circular 41.13, but it’s slightly heavier and is more difficult to find.

For Sitka spruce to meet government specification MIL-S-6073, it goes through a series of inspections, starting with experts who supervise the sawing and milling of the lumber at the source. The lumber is kiln-dried to another government specification, AN-W-2. This spec says the wood must have a specific gravity greater than .36, a minimum density of 24 pounds per cubic foot, grain slope no steeper than one in 15, and a moisture content between 10 and 17 percent. This Type A wood is approved for use in any aircraft application, including use as supercritical spar material. Type B specs-lumber that is slightly less dense and may have more grain slope-can still be used in some applications, but not in any primary load structures.

Plywood is another common aircraft building material. It covers the wings of the aerobatic One Design and the fuselage of the Falco, and the gussets that strengthen wood wing ribs and fuselage structures are made from it. This is not hardware-store-variety plywood, mind you, but Mil-Spec aircraft-grade made from imported African mahogany or American birch veneers laminated in a hot press using waterproof glues. The core of aircraft-grade plywood is usually poplar or basswood.

Lest you think corrosion is something that only happens to metal, wood can also develop a sort of organic rust. Known as dry rot, this fungus is caused by too much moisture content and can render wood unusable. So when you store your wood-especially if your building project will span the course of several years-keep it in a well-ventilated area. A place with about 12 to 15 percent relative humidity is best, because wood that gets too dry can become brittle.

 

Alternatives to Sitka Spruce  (Ref: Article from Sport Aviation December, 1998 by Ron Alexander)


If Sitka Spruce is so difficult to obtain why not find alternatives? A valid question and certainly a number of alternatives to spruce do exist. First of all, lets look at what type of wood can be used to replace spruce within an aircraft structure. Understand that written information regarding the use of wood in aircraft is limited.

The primary source of information for the builder may be obtained from FAA Advisory Circular 43-13, government bulletin ANC-19, and from a copy of Mil-Spec-6073. Advisory Circular 43-13 lists a number of different types of wood that may be used in an aircraft structure. Some of these are Douglas Fir, Noble Fir, Western Hemlock, White Pine, White Cedar, and Yellow Poplar. I will discuss the ones that are the most readily available—Douglas Fir, White Pine, and Western Hemlock.


As noted in the comparison chart in Figure 1, Douglas Fir is a very acceptable alternative for spruce. Its strength exceeds spruce by roughly 23%. Advisory Circular 43-13 states that it may be used as a substitute for spruce in same sizes or slightly reduced sizes providing the reduction in size is substantiated.

Fir does have a tendency to split making it somewhat more difficult to work. It is also heavier than spruce—about 26% heavier in fact. Remember, you are allowed to use a smaller dimension due to the increased strength. Years ago, a number of aircraft manufacturers would route out a portion of a fir spar to save weight.

Boeing used that method on a number of PT-13 and PT-17 trainers.

Can you purchase good Douglas Fir? Some lumberyards will have a good supply at a reasonable price. Most aircraft supply companies find it just as difficult to obtain Douglas Fir as they do Sitka Spruce.

The cost from an aircraft supply company will be about the same. You may find Douglas Fir cheaper at a lumberyard.

What about White Pine? As you can see from the chart White Pine is 85-96% as strong as spruce. It is easy to work with and is somewhat available. A number of kit manufacturers are using White Pine successfully within their designs. It is low in hardness and shock resisting capability. It cannot be used as a direct substitute for spruce without an increase in size to compensate for the lesser strength.

Western Hemlock has been used in the construction of aircraft for a number of years. The popular Pietenpol airplane used Western Hemlock in constructing spars for a number of years.
The strength properties slightly exceed spruce and the wood may be used as a direct substitute for spruce. FAA Advisory Circular 43-13 notes that it is less uniform in texture than spruce.


Concerning the comparison chart in Figure 1, two definitions are in order. A ring per inch is a measure of the rate of diameter growth of a tree. These rings correspond closely to yearly increments of growth of the tree. See Figure 2. They are not necessarily definite criteria for
strength. Mil-Spec-6073 defines the number of rings per inch needed for spruce that will be used in an aircraft structure. According to government bulletin ANC-19 – Wood Aircraft Inspection and Fabrication—it states "Rejection of material on the basis of the number of rings per inch is somewhat arbitrary, because it does not always reflect the strength of the piece."
Maximum grain slope is the deviation of annual growth rings from parallelism with the longitudinal axis of a piece of wood. See Figure 3. Looking at the face of a board the growth rings should not slope upward or downward more than the specified amount, usually 1 inch in a
15-inch length of the wood. This slope of grain is usually termed diagonal grain. Both of these will be discussed in detail in the section pertaining to inspection of wood.


CHART OF WOODS FOR AIRCRAFT USE 
TYPE OF WOOD           STRENGTH           MINIMUM RINGS PER INCH            MAXIMUM GRAIN SLOPE
Sitka Spruce                 100%                                              6                                                    1:15
Douglas Fir                   Exceeds Spruce                             8                                                    1:15
White Pine                    85-96%                                          6                                                     1:15
Western Hemlock        Slightly exceeds spruce               6                                                    1:15

INSPECTING WOOD FOR AIRCRAFT USE
If I cannot obtain spruce or any other wood that is certified for use on aircraft how do I know I have the correct quality?

The answer is you don’t. You must find someone familiar with inspecting wood or learn more about it yourself.

Now, there is certainly a difference between production aircraft and experimental aircraft concerning legalities.

There is, however, no difference in concerns for high quality.
Production aircraft must verify a source for all materials that are used as a replacement for original parts.

That means very simply that you should be able to track the origin of the wood that you will be using to replace a spar in a production airplane, as an example. Since wood is not stamped "certified for aircraft use" what does the FAA want in the form of paperwork to
verify you are placing the proper type of wood on your airplane? Most of the inspectors I have contacted agree that a copy of the grading certificate stating that the shipment of wood that included your spar material meets Mil-Spec-6073.

As far as actually certifying the wood as being legal to be placed upon your airplane that is the responsibility of the A & P mechanic and
ultimately the IA who returns the aircraft to service after the repair.

Some companies will actually manufacture a spar for replacement on a certain type of airplane.

This should be done using a PMA number (Parts Manufacturing Authority).

That satisfies the requirement for origin of the part but it must still be inspected and authorized by the IA.
As you are probably aware, the materials used in experimental aircraft do not have to meet any legal requirements.

That does not exempt the builder from using common sense and good judgement.

In other words, even though I do not have to verify the origin of the wood used in an experimental aircraft I will want to do so.

I would strongly encourage the builder to thoroughly inspect the final piece of wood for defects prior to installation.

Now, the builder of an experimental aircraft can go to a local lumber yard and purchase spruce, fir, or white pine.

If you are purchasing spruce make sure it is Sitka Spruce. No grading certificate is required and usually cannot be obtained because an expert does not grade that wood. There is nothing wrong with purchasing wood from a lumberyard as long as you know what you are buying. In other words, you must become familiar with allowable defects and tolerances regarding the use of wood in aircraft.

This will be accomplished by acquiring information through AC43-13, ANC-19, Mil-Spec-6073, etc. to ensure you know what is safe in your airplane. If you do not feel confident in performing this inspection, find someone who is knowledgeable concerning aircraft wood.
I will outline the proper procedure for identifying and inspecting wood for use in aircraft. This will help you familiarize yourself enough with the major defects to be able to identify them and know that the wood you are using is safe. I will be quoting largely from Mil-Spec-6073, a document that can be purchased through Aircraft Spruce & Specialty. The Forest Products Laboratory also has a wealth of information concerning wood in general. They have been very helpful to the EAA and to custom builders in general. Ben Owen and his group of knowledgeable people in Information Services at EAA Headquarters also have a lot of good information regarding aircraft wood.